The Effect of Beverage Type and Exposure Duration on Bond Strength Between Zirconia- Based CAD/CAM Ceramic and Resin Cement
DOI:
https://doi.org/10.15517/rv7tx995Keywords:
Zirconia; Resin cement; Bond strength; Beverages; Aging.Abstract
This in vitro study aimed to evaluate the effects of beverages with different pH levels and various storage durations on the shear bond strength (SBS) of CAD-CAM zirconia bonded with dual-cure resin cement. A total of ninety specimens were prepared using CAD-CAM zirconia (Katana Zirconia, Kuraray, Japan) and a dual-cure resin cement (Panavia V5, Kuraray, Japan). The specimens were randomly divided into three groups according to the storage solution: distilled water, mineral water, and cola. Each group was further subdivided into three time intervals: 24 hours, 30 days, and 90 days (n=10 per subgroup). All specimens were stored at room temperature and exposed to the respective solution for 20 minutes daily. Shear bond strength testing was performed using a universal testing machine, and the results were analyzed by one-way ANOVA at a significance level of α=0.05. The statistical analysis revealed no significant effect of the type of beverage (p=0.114), storage time (p=0.214), or the interaction between them (p=0.433) on SBS values. Although the lowest bond strength was observed in specimens stored in cola for 90 days (11.95±3.32 MPa), this difference was not statistically significant. The highest value was recorded in the distilled water group at 24 hours (18.65±5.93 MPa). Within the limitations of this study, the type of beverage and exposure duration did not significantly affect the shear bond strength of the zirconia-resin cement interface. However, acidic beverages such as cola may demonstrate a trend toward decreased bond strength following prolonged exposure.
Downloads
References
Blatz M.B., Conejo J. The current state of chairside digital dentistry and materials. Dent Clin North Am. 2019; 63 (2): 175-197. DOI: https://doi.org/10.1016/j.cden.2018.11.002
Mainjot A., Dupont N.M., Oudkerk J.C., Dewael T.Y., Vanheusden A.J. From artisanal to CAD CAM blocks: State of the art of indirect composites. J Dent Res. 2016; 95 (5): 487-495. DOI: https://doi.org/10.1177/0022034516634286
Giordano R. II. Ceramics overview. Br Dent J. 2022; 232 (9): 658 663. DOI: https://doi.org/10.1038/s41415-022-4242-6
Sailer I., et al. All ceramic partial coverage restorations-material selection and clinical performance. J Adhes Dent. 2015; 17 (4): 303-320.
Zhang Y., Lawn B.R. Novel zirconia materials in dentistry. J Dent Res. 2018; 97 (2): 140-147. DOI: https://doi.org/10.1177/0022034517737483
Özcan M., Vallittu P.K. Effect of surface conditioning methods on the bond strength of luting cement to ceramics. Dent Mater. 2003; 19 (8): 725 731. DOI: https://doi.org/10.1016/S0109-5641(03)00019-8
Kern M., Wegner S.M. Bonding to zirconia ceramic: adhesion methods and their durability. Dent Mater. 1998; 14 (1): 64-71. DOI: https://doi.org/10.1016/S0109-5641(98)00011-6
Matinlinna J.P., et al. The effect of a MDP containing primer on resin bond strength to zirconia. Dent Mater. 2013; 29 (3): 241-248.
Aboushelib M.N., et al. Influence of surface treatment and cyclic loading on the bond strength of zirconia to resin cement. J Prosthet Dent. 2010; 103 (4): 210-217. DOI: https://doi.org/10.1016/S0022-3913(10)60033-9
Al Amri M.D., Ahmed K.E., Al Moaleem M.M. Evaluation of the effect of soft drinks on the surface roughness of dental enamel. F1000Res. 2021; 10: 1090.
Tseng T.C., et al. Surface degradation effects of carbonated soft drink on a resin based dental compound. Heliyon. 2021; 7 (3): e06592.
Larsen M.J., Nyvad B. Enamel erosion by some soft drinks and orange juices relative to their pH, buffering effect, and contents of calcium phosphate. Caries Res. 1999; 33 (1): 81-87. DOI: https://doi.org/10.1159/000016499
Colombo M., et al. Vickers micro hardness of new restorative CAD/CAM dental materials: evaluation after exposure to acidic drink. Materials. 2019; 12 (8): 1246. DOI: https://doi.org/10.3390/ma12081246
Yiğit D., et al. Effect of various beverages on adhesion of repaired CAD/CAM restorative materials. J Funct Biomater. 2023; 14 (7): 380. DOI: https://doi.org/10.3390/jfb14070380
Szalewski L., Wójcik D., Bogucki M., Szkutnik J., Różyło Kalinowska I. The Influence of Popular Beverages on Mechanical Properties of Composite Resins. Materials (Basel). 2021; 14 (11): 3097. DOI: https://doi.org/10.3390/ma14113097
Bahadır H.S., Bayraktar Y. Evaluation of the repair capacities and color stabilities of a resin nanoceramic and hybrid CAD/CAM blocks. J Adv Prosthodont. 2020; 12 (3): 140-149. DOI: https://doi.org/10.4047/jap.2020.12.3.140
Taji S., Seow W.K. A literature review of dental erosion in children. Aust Dent J. 2010; 55 (4): 358 367. DOI: https://doi.org/10.1111/j.1834-7819.2010.01255.x
Cochrane N.J., Yuan Y., Walker G.D., Shen P., Reynolds E.C. Erosive potential of beverages sold in Australian schools. Aust Dent J. 2009; 54 (3): 238-244. DOI: https://doi.org/10.1111/j.1834-7819.2009.01126.x
Al Amri M.D., Ahmed K.E., Al Moaleem M.M. Evaluation of the effect of soft drinks on the surface roughness of dental enamel in natural human teeth. F1000Res. 2021;10: 1090. DOI: https://doi.org/10.12688/f1000research.55556.1
Tseng T.C., Kuo C.Y., Chen Z.Y., Hsieh K.C. Surface degradation effects of carbonated soft drink on a resin based dental compound. Heliyon. 2021; 7 (3): e06592. DOI: https://doi.org/10.1016/j.heliyon.2021.e06400
Iosif L., Enache M.A., Ionescu M., Popa D. Effects of acidic environments on dental structures after bracket debonding. Int J Mol Sci. 2022; 23 (24): 15586. DOI: https://doi.org/10.3390/ijms232415583
Khoda B., Ansari A., Tavakoli M. The effect of different soft drinks on the shear bond strength of orthodontic brackets. J Dent (Tehran). 2012; 9 (2): 145 149.
Castillejos Cartas L., Sáez Espínola G., Álvarez Gayosso C., Herrera Chávez M.G. Bond strength of brackets bonded with resin in contact with an alcoholic beverage. Rev Mex Ortod. 2014; 2 (3): e166 e169. DOI: https://doi.org/10.1016/S2395-9215(16)30143-X
Uğur M., Kavut İ., Tanrıkut Ö.O., Cengiz Ö. Effect of ceramic primers with different chemical contents on the shear bond strength of CAD/CAM ceramics with resin cement after thermal ageing. BMC Oral Health. 2023; 23 (1): 210. DOI: https://doi.org/10.1186/s12903-023-02909-z
Cao Y., Zhang J.F., Ou X., Zhang B., Chen L., Deng X.H. The effects of four primers and two cement types on the bonding strength of zirconia. Ann Transl Med. 2022; 10 (5): 248. DOI: https://doi.org/10.21037/atm-21-4909
Published
Issue
Section
License
Copyright (c) 2025 Goktug Yersel, Engin Sacu, Neslihan Tekce.
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.
ODOVTOS - Int. J. Dent. Sc. endorses CC BY-NC-SA
This license enables reusers to distribute, remix, adapt, and build upon the material in any medium or format for noncommercial purposes only, and only so long as attribution is given to the creator. If you remix, adapt, or build upon the material, you must license the modified material under identical terms. CC BY-NC-SA includes the following elements:
BY: credit must be given to the creator.
NC: Only noncommercial uses of the work are permitted.
SA: Adaptations must be shared under the same terms.