In Vitro Effect of Temperature on Dentin Bond Strength of Universal Adhesive Systems
DOI:
https://doi.org/10.15517/ijds.2020.39198Keywords:
Shear bond strength; Universal adhesive systems; Preheating.Abstract
The aim of this study was to evaluate the shear bond strength (SBS) of two universal adhesives (Universal Single Bond and All Bond Universal) and a two-step self-etch adhesive system (Clearfil SE Bond) to dentine at various temperatures. Materials and Methods: One hundred and twenty dentin specimens were divided randomly to 12 groups, according to adhesive systems (Universal Single Bond and All Bond Universal, Clearfil SE Bond) and temperature ( 4ºC, 20 ºC, 36ºC, 55ºC) used. Dentin specimens were prepared (n :10, adhesives were applied, and composite cylinders were polymerized. Statistical analysis of the SBS data was performed using Two-way analysis of variance (ANOVA) and Tukey’s Honestly Significant Differences post-hoc test. Results: The Clearfil SE Bond was shown to have higher SBS than the universal adhesives at all temperatures; however, there was no statistically significant difference (P>0.05). In both groups, the lowest SBS values were observed in the samples at 4°C while the highest SBS values were observed in the samples at 55°C. In this case, there was a statistically significant difference (P<0.05). Conclusions: The results suggest that the effectiveness of an adhesive may increase if it is preheated at 36°C or above before use instead of being used immediately after removal from the refrigerator or at room temperature.
Downloads
References
Münchow E. A., Valente L. L., Bossardi M., Priebe T. C., Zanchi C. H., Piva E. Influence of surface moisture condition on the bond strength to dentin of etch-and-rinse adhesive systems. Braz J of Oral Sci 2014; 13: 182-186. DOI: https://doi.org/10.1590/1677-3225v13n3a04
Van Meerbeek B, De Munck J, Yoshida Y, Inoue S, Vargas M, Vijay P, et al. Adhesion to enamel and dentin: current status and future challenges. Oper Dent 2003; 28: 215-235.
Van Meerbeek B, Yoshihara K, Yoshida Y, Mine A, De Munck J, Van Landuyt K. State of the art of self-etch adhesives. Dent Mater 2011; 27: 17-28. DOI: https://doi.org/10.1016/j.dental.2010.10.023
Hanabusa M, Mine A, Kuboki T, Momoi Y, Van Ende A, Van Meerbeek B, et al. Bonding effectiveness of a new ‘multi-mode’ adhesive to enamel and dentin. J Dent 2012; 40: 475-484. DOI: https://doi.org/10.1016/j.jdent.2012.02.012
Yoshihara K., Yoshida Y., Nagaoka N., Fukegawa D., Hayakawa S., Mine A., et al. Nano-controlled molecular interaction at adhesive interfaces for hard tissue reconstruction. Acta Biomater 2010; 6: 3573-3582. DOI: https://doi.org/10.1016/j.actbio.2010.03.024
Mutluay M. M., Yahyazadehfar M., Ryou H., Majd H., Do D., Arola D. Fatigue of the resin–dentin interface: A new approach for evaluating the durability of dentin bonds. Dent Mater 2013; 29: 437-449. DOI: https://doi.org/10.1016/j.dental.2013.01.008
Chiba Y., Miyazaki M., Rikuta A., Moore B. Influence of environmental conditions on dentin bond strengths of one-application adhesive systems. Oper Dent 2004; 29: 554-559.
Toledano M., Osorio R., Albaladejo A., Aguilera F. S., Osorio E. Differential effect of in vitro degradation on resin–dentin bonds produced by self etch versus total etch adhesives. J Biomed Mater Res A: An Official Journal of The Society for Biomaterials, The Japanese Society for Biomaterials, and The Australian Society for Biomaterials and the Korean Society for Biomaterials 2006; 77: 128-135. DOI: https://doi.org/10.1002/jbm.a.30656
Perdigão J., Sezinando A., Monteiro P. C. Laboratory bonding ability of a multi-purpose dentin adhesive. Am J Dent 2012; 25: 153-158.
Muñoz M. A., Luque I., Hass V., Reis A., Loguercio A. D., Bombarda NHC. Immediate bonding properties of universal adhesives to dentine. J Dent 2013; 41: 404-411. DOI: https://doi.org/10.1016/j.jdent.2013.03.001
Yoshioka M., Yoshida Y., Inoue S., Lambrechts P., Vanherle G., Nomura Y., et al. Adhesion/decalcification mechanisms of acid interactions with human hard tissues. J Biomed Mater Res: An Official Journal of The Society for Biomaterials and The Japanese Society for Biomaterials. 2002; 59: 56-62. DOI: https://doi.org/10.1002/jbm.1216
Fukuda R., Yoshida Y., Nakayama Y., Okazaki M., Inoue S., Sano H., et al. Bonding efficacy of polyalkenoic acids to hydroxyapatite, enamel and dentin. Biomaterials 2003; 24: 1861-1867. DOI: https://doi.org/10.1016/S0142-9612(02)00575-6
Loguercio A., Salvalaggio D., Piva A., Klein-Júnior C., de Lr Accorinte M., Meier M., et al. Adhesive temperature: effects on adhesive properties and resin-dentin bond strength. Oper Dent 2011; 36: 293-303. DOI: https://doi.org/10.2341/10-218L
Reis A., Klein-Júnior C., de Souza F. C., Stanislawczuk R, Loguercio A. The use of warm air stream for solvent evaporation: effects on the durability of resin-dentin bonds. Oper Dent 2010; 35: 29-36. DOI: https://doi.org/10.2341/08-065-L
Vale M., Afonso F., Borges B., Freitas Jr. A., Farias-Neto A, Almeida E, et al. Preheating impact on the degree of conversion and water sorption/solubility of selected single-bottle adhesive systems. Oper Dent 2014; 39: 637-643. DOI: https://doi.org/10.2341/13-201-L
Sadr A., Ghasemi A., Shimada Y., Tagami J. Effects of storage time and temperature on the properties of two self-etching systems. J Dent 2007; 35: 218-225. DOI: https://doi.org/10.1016/j.jdent.2006.08.004
Hisamatsu N., Atsuta M., Matsumura H. Effect of silane primers and unfilled resin bonding agents on repair bond strength of a prosthodontic microfilled composite. J Oral Rehabil 2002; 29: 644-648. DOI: https://doi.org/10.1046/j.1365-2842.2002.00899.x
Abate P., Rodriguez V., Macchi R. Evaporation of solvent in one-bottle adhesives. J Dent 2000; 28: 437-440. DOI: https://doi.org/10.1016/S0300-5712(00)00018-X
Daronch M., Rueggeberg F., De Goes M., Giudici R. Polymerization kinetics of pre-heated composite. J Dent Res 2006; 85: 38-43. DOI: https://doi.org/10.1177/154405910608500106
Blalock J. S., Holmes R. G., Rueggeberg F. A. Effect of temperature on unpolymerized composite resin film thickness. J Prosthet Dent 2006; 96: 424-432. DOI: https://doi.org/10.1016/j.prosdent.2006.09.022
Pazinatto F. B., Marquezini Jr. L., Atta MT. Influence of Temperature on the Spreading Velocity of Simplified Step Adhesive Systems. J Esthet Restor Dent 2006; 18: 38-46. DOI: https://doi.org/10.2310/6130.2006.00009
De Munck Jd, Van Landuyt K., Peumans M., Poitevin A., Lambrechts P., Braem M., et al. A critical review of the durability of adhesion to tooth tissue: methods and results. J Dent Res 2005; 84: 118-132. DOI: https://doi.org/10.1177/154405910508400204
Korkmaz Y., Gurgan S., Firat E., Nathanson D. Shear bond strength of three different nano-restorative materials to dentin. Oper Dent 2010; 35: 50-57. DOI: https://doi.org/10.2341/09-051-L
Nam K.-Y., Kim J.-B., Jang B.-C., Kwon T.-Y., Kim K.-H. Effects of dentin bonding agents on bonding durability of a flowable composite to dentin. Dent Mater J 2007; 26: 224-231. DOI: https://doi.org/10.4012/dmj.26.224
Published
Issue
Section
License
Copyright (c) 2019 Serdar Akarsu DDS, PhD, Sultan Aktuğ Karademir DDS (Author)
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.
ODOVTOS - Int. J. Dent. Sc. endorses CC BY-NC-SA
This license enables reusers to distribute, remix, adapt, and build upon the material in any medium or format for noncommercial purposes only, and only so long as attribution is given to the creator. If you remix, adapt, or build upon the material, you must license the modified material under identical terms. CC BY-NC-SA includes the following elements:
BY: credit must be given to the creator.
NC: Only noncommercial uses of the work are permitted.
SA: Adaptations must be shared under the same terms.