Keywords
concrete, resistance to compression, modified cement, aggregates
How to Cite
Abstract
This paper presents a synthesis of the experimental results obtained from testing the evolution of the compressive strength in concrete made with different modified cements at different ages. It includes the characterization of two aggregates of different provenances (river and quarry) and three types of modified cements. The cements tested correspond to MM/C (P-C) -28, MM/C (C-P) -28 and MC/A - AR. The objective of the study was to generate the standard resistance development curves of six concrete mixtures (in percentage terms), using these cements and aggregates. The characterization tests were conducted out following the INTECO and ASTM standards. The curing of concrete specimens took place in a humid chamber at 4 different ages (3, 7, 28 and 56 days). The strength of the concrete was obtained through tests on the Universal Machine, and the results were processed and validated statistically, using the acceptance parameters of the ACI 214-2002 report. From the analysis, it was possible to generate the curves of standard development of resistance for all the cements under study using two provenances of aggregates, including an inferential statistical analysis for the resistance results of the concretes. It was concluded that, by varying the origin of the aggregate for the same cement, the resistance of the concrete is significantly different (on statistical terms), as for the same aggregate when the type of cement is changed.
References
Decreto Ejecutivo N° 39414-MEIC-S Reglamento Técnico RTCR 479:2015 Materiales de Construcción, Cementos Hidráulicos.
Instituto Americano del Concreto. (2002). ACI 214 Evaluación de los resultados de resistencia del concreto. American Concrete Institute: Michigan, Estados Unidos de América.
Instituto de Normas Técnicas de Costa Rica. (2014). INTE C15:2014. Agregados para concreto – Requisitos.
Instituto de Normas Técnicas de Costa Rica (2016). INTE C18:2016. Práctica normalizada para preparación y curado de especímenes de concreto para ensayo en laboratorio.
Instituto de Normas Técnicas de Costa Rica. (2016). INTE C29:2016. Método de prueba para determinar el porcentaje de partículas fracturadas en el agregado.
Instituto de Normas Técnicas de Costa Rica. (2016). INTE C39:2016. Método estándar de prueba para la resistencia a la compresión de elementos cilíndricos de concreto.
Instituto de Normas Técnicas de Costa Rica. (2008). INTE C57:2008. Método de ensayo para la resistencia a la compresión de morteros de cemento hidráulico — Usando especimenes cúbicos de 50 mm.
Instituto de Normas Técnicas de Costa Rica. (2013). INTE C58:2013. Método de ensayo normalizado para determinar la densidad aparente o peso unitario y porcentaje de vacíos en los agregados.
Instituto de Normas Técnicas de Costa Rica. (2015). INTE C59:2015. Método de ensayo normalizado para la detección de impurezas orgánicas en el agregado fino para el concreto.
Instituto de Normas Técnicas de Costa Rica. (2015). INTE C62:2015. Especificación estándar para la reducción de muestras de agregados para ensayos.
Instituto de Normas Técnicas de Costa Rica. (2009). INTE C64:2009. Determinación de la resistencia al desgaste de los agregados gruesos hasta de 37,5 mm, utilizando la máquina De Los Ángeles.
Instituto de Normas Técnicas de Costa Rica. (2015). INTE C67:2015. Práctica para la toma de muestras de agregados.
Instituto de Normas Técnicas de Costa Rica. (2016). INTE C68:2016. Método de ensayo para la determinación de la densidad relativa (gravedad específica) y la absorción del agregado grueso.
Instituto de Normas Técnicas de Costa Rica. (2016). INTE C69:2016. Método de ensayo para la determinación de la densidad relativa (gravedad específica) y la absorción del agregado fino.
Instituto de Normas Técnicas de Costa Rica. (2012). INTE C137:2012. Método de ensayo para la determinación del tiempo de fragua de un cemento hidráulico por medio de la aguja de Vicat.
Instituto de Normas Técnicas de Costa Rica. (2011). INTE C139:2011. Método de ensayo para la determinación de la consistencia normal del cemento hidráulico.
Instituto de Normas Técnicas de Costa Rica. (2012). INTE C141:2012. Método de ensayo para la determinación de la densidad del cemento hidráulico.
Instituto de Normas Técnicas de Costa Rica. (2016). INTE C142:2016. Método de ensayo para la determinación de la finura de un cemento hidráulico por medio de la malla de 45 m (N° 325).
Instituto de Normas Técnicas de Costa Rica. (2015). INTE C147:2015. Cemento hidráulico – Requisitos.
Instituto de Normas Técnicas de Costa Rica. (2015). INTE C153:2015. Extracción de muestras y cantidad de ensayos para cemento hidráulico.